引(yin)言

    因為偏光(guang)片在LCD的(de)(de)外(wai)層，它的(de)(de)失效會讓人(ren)眼看到，所以偏光(guang)片的(de)(de)可(ke)靠(kao)(kao)性(xing)對LCD非常(chang)重要。如何驗證偏光(guang)片的(de)(de)可(ke)靠(kao)(kao)性(xing)，如何對比評價偏光(guang)片可(ke)靠(kao)(kao)性(xing)，是LCD工(gong)廠(chang)需(xu)要了解和(he)解決的(de)(de)問題。

    1、現象(xiang)分析

    偏光片的(de)失效現象主要有以(yi)下幾種：

    (1)偏(pian)(pian)光(guang)(guang)片(pian)(pian)(pian)與玻(bo)璃(li)(li)分層：表(biao)現的現象(xiang)為偏(pian)(pian)光(guang)(guang)片(pian)(pian)(pian)從玻(bo)璃(li)(li)上翹起(qi)，偏(pian)(pian)光(guang)(guang)片(pian)(pian)(pian)與玻(bo)璃(li)(li)之(zhi)間出(chu)(chu)現氣泡，偏(pian)(pian)光(guang)(guang)片(pian)(pian)(pian)出(chu)(chu)現偏(pian)(pian)光(guang)(guang)片(pian)(pian)(pian)亮線。具體現象(xiang)可參考圖1、圖2。

    (2)偏光片(pian)(pian)的偏光效率降(jiang)低，嚴重(zhong)時出現偏光片(pian)(pian)發白或發黃變色現象(xiang)，具體現象(xiang)可參見圖3、圖4。

    (3)偏光片各層之間分開，參見圖5。

    2、原(yuan)因分析

    出現偏(pian)光片(pian)失效的(de)(de)原因，是偏(pian)光片(pian)承受(shou)不(bu)了惡(e)劣的(de)(de)環境(jing)，或者偏(pian)光片(pian)的(de)(de)質量比較(jiao)低。按照偏(pian)光片(pian)可靠性等(deng)級可以分為普通偏(pian)光片(pian)、中耐(nai)久偏(pian)光片(pian)和高耐(nai)久偏(pian)光片(pian)。
    普通偏光片(pian)40℃，90% RH
    中耐久偏(pian)光片(pian)60℃ ， 90% RH
    高耐久偏光(guang)片80℃，90% RH
    但是實(shi)際使用只按照以，上的(de)(de)分級進(jin)行偏光片選擇(ze)使用，無法滿足各(ge)(ge)種(zhong)(zhong)各(ge)(ge)樣的(de)(de)產品要求(qiu)，當條件超出(chu)以上條件時就會出(chu)現無法預料的(de)(de)情況。我們(men)對(dui)比了(le)不(bu)，同生產廠的(de)(de)偏光片性能(neng)，并且對(dui)造成(cheng)各(ge)(ge)種(zhong)(zhong)失效的(de)(de)原因進(jin)行了(le)實(shi)驗分析。
    下面來討論偏(pian)光(guang)片可(ke)(ke)靠(kao)性(xing)驗(yan)證中出(chu)(chu)現的(de)(de)問題(ti)及如何(he)更(geng)好地辨(bian)別偏(pian)光(guang)片的(de)(de)優劣。將偏(pian)光(guang)片裁切成(cheng)一定(ding)尺寸的(de)(de)小片，貼到玻(bo)璃(li)上，經(jing)過脫泡后(hou)，揭掉偏(pian)光(guang)片的(de)(de)保護膜(mo)，進行高低溫濕(shi)熱試驗(yan)箱(xiang)、紫外線(xian)老化試驗(yan)等相關的(de)(de)可(ke)(ke)靠(kao)性(xing)實(shi)驗(yan)。我們結合終客戶的(de)(de)使用情況(kuang)及反饋(kui)的(de)(de)實(shi)驗(yan)現象(xiang)，分(fen)析(xi)摸索出(chu)(chu)各種失(shi)效(xiao)現象(xiang)產生的(de)(de)原因(yin)，以及如何(he)驗(yan)證處不良的(de)(de)失(shi)效(xiao)現象(xiang)。具體(ti)如下：
    (1)偏光片與玻璃分層，出現偏光片翹起，亮線等出現此種現象的原因，認為此種現象與偏光片的膠水層有關，亮線是偏光片與玻璃分層后再冷卻的過程中出現的，也可以認為是偏光片的翹起。對普通級偏光片放置高低溫濕熱試驗箱內，分別用40℃，90% RH；60℃ ， 90% RH；80℃，90% RH進行驗證，從不同生產廠家的偏光片來看，壓敏膠質量好的偏光片工廠生產的普通偏光片放置高低溫濕熱試驗箱內，按照40℃，90% RH；60℃，90% RH；條件分別做120小時的驗證，沒有出現偏光片變白的失效現象，也不會出現偏光片翹起和亮線的現象。而把條件提高到80℃，90% RH，120小時，此時就會出現偏光片的變白失效現象，但是仍然不會出現偏光片的翹起，亮線現象。而對于一些壓敏膠質量差的偏光片放置高低溫濕熱試驗箱內，也按40℃，90% RH；60℃，90% RH  120小時的條件分別做可靠性驗證，實驗后沒有出現偏光片變白的失效現象，但是都出現翹起和亮線現象。按照60℃，90% RH條件實驗的失效現象更嚴重，在12小時后就出現了亮線現象。并且通過對一些庫存時間比較長，超過有效期的偏光片，進行以上條件的驗證，也可以發現以上現象。
    (2)偏光(guang)片發黃(huang)
    將偏光片不貼到玻璃上，通過UV紫外線老化試驗箱，偏光片會出現變黃收縮的現象，而把偏光片貼到玻璃上通過UV紫外線老化試驗箱就不會出現變黃的現象。另外，貼到玻璃.上的偏光片進行超過150℃的烘烤也會出現偏光片的變黃現象。結合以上的實驗認為，UV光不會引起偏光片的變黃，通過UV變黃的原因是因為UV光照射過程中產生了過高的溫度所導致。所以，出現偏光片變黃現象的主要原因是偏光片承受了過高的溫度。
    (3)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)分層(ceng)(ceng)(ceng)(ceng)，嚴(yan)重(zhong)時偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)變(bian)(bian)白，偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)層(ceng)(ceng)(ceng)(ceng)變(bian)(bian)色收縮對(dui)于客戶反饋出(chu)(chu)(chu)的(de)(de)(de)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)分層(ceng)(ceng)(ceng)(ceng)現(xian)象(xiang)，對(dui)不良的(de)(de)(de)普通偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)分別(bie)做(zuo)不同的(de)(de)(de)溫度(du)條件(jian)40℃，90% RH；60℃ ， 90% RH；80℃，90% RH  48小時的(de)(de)(de)實(shi)驗(yan)。實(shi)驗(yan)后，前兩種偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)仍然完好無損，80℃，90%RH 48小時的(de)(de)(de)實(shi)驗(yan)，偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)變(bian)(bian)白，但是(shi)沒(mei)有(you)出(chu)(chu)(chu)現(xian)分層(ceng)(ceng)(ceng)(ceng)現(xian)象(xiang)。用以上的(de)(de)(de)條件(jian)無法(fa)(fa)對(dui)分層(ceng)(ceng)(ceng)(ceng)現(xian)象(xiang)進行判別(bie)。我們通過摸索，采用水浸(jin)泡(pao)(pao)的(de)(de)(de)方法(fa)(fa)才能重(zhong)現(xian)此種現(xian)象(xiang)，實(shi)驗(yan)條件(jian)是(shi)40℃ ，水浸(jin)泡(pao)(pao)。實(shi)驗(yan)結果，浸(jin)泡(pao)(pao)到2小時后不良的(de)(de)(de)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)就會出(chu)(chu)(chu)現(xian)分層(ceng)(ceng)(ceng)(ceng)現(xian)象(xiang)，偏(pian)(pian)光(guang)(guang)(guang)層(ceng)(ceng)(ceng)(ceng)開始收縮，比較(jiao)好的(de)(de)(de)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)沒(mei)有(you)變(bian)(bian)化。4小時后不良的(de)(de)(de)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)會出(chu)(chu)(chu)現(xian)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)各(ge)層(ceng)(ceng)(ceng)(ceng)完全分開， PVC層(ceng)(ceng)(ceng)(ceng)完全失效變(bian)(bian)白，比較(jiao)好的(de)(de)(de)偏(pian)(pian)光(guang)(guang)(guang)片(pian)(pian)(pian)出(chu)(chu)(chu)現(xian)輕微的(de)(de)(de)分層(ceng)(ceng)(ceng)(ceng)現(xian)象(xiang)。

    3、結論(lun)

    (1)偏(pian)光片與玻璃分層， 出現(xian)偏(pian)光片翹起，亮(liang)線的現(xian)象(xiang)可(ke)以用潮(chao)熱(re)實(shi)驗(yan)的方(fang)(fang)法進(jin)行驗(yan)證(zheng)，為加快速(su)度(du)可(ke)以用提高(gao)溫濕度(du)條件(jian)的方(fang)(fang)法加速(su)失效現(xian)象(xiang)的出現(xian)；
    (2)偏光片(pian)發(fa)黃(huang)的(de)(de)現象，可以用高溫的(de)(de)方法進行驗(yan)證；
    (3)偏光片(pian)分層(ceng)，嚴(yan)重時偏光片(pian)變(bian)白(bai)，偏光片(pian)層(ceng)出現變(bian)色收縮，此種現象可以用40℃水浸泡4小時的方法進行驗證。